3D printable elastomers with exceptional strength and toughness
成果类型：
Article
署名作者：
Fang, Zizheng; Mu, Hongfeng; Sun, Zhuo; Zhang, Kaihang; Zhang, Anyang; Chen, Jiada; Zheng, Ning; Zhao, Qian; Yang, Xuxu; Liu, Feng; Wu, Jingjun; Xie, Tao
署名单位：
Zhejiang University; Zhejiang University; Zhejiang University; Shanghai Jiao Tong University; Zhejiang University
刊物名称：
Nature
ISSN/ISSBN：
0028-5573
DOI：
10.1038/s41586-024-07588-6
发表日期：
2024-07-25
关键词：
interface
摘要：
Three-dimensional (3D) printing has emerged as an attractive manufacturing technique because of its exceptional freedom in accessing geometrically complex customizable products. Its potential for mass manufacturing, however, is hampered by its low manufacturing efficiency (print speed) and insufficient product quality (mechanical properties). Recent progresses in ultra-fast 3D printing of photo-polymers1-5 have alleviated the issue of manufacturing efficiency, but the mechanical performance of typical printed polymers still falls far behind what is achievable with conventional processing techniques. This is because of the printing requirements that restrict the molecular design towards achieving high mechanical performance. Here we report a 3D photo-printable resin chemistry that yields an elastomer with tensile strength of 94.6 MPa and toughness of 310.4 MJ m-3, both of which far exceed that of any 3D printed elastomer6-10. Mechanistically, this is achieved by the dynamic covalent bonds in the printed polymer that allow network topological reconfiguration. This facilitates the formation of hierarchical hydrogen bonds (in particular, amide hydrogen bonds), micro-phase separation and interpenetration architecture, which contribute synergistically to superior mechanical performance. Our work suggests a brighter future for mass manufacturing using 3D printing. Three-dimensional photo-printable resin chemistry yields an elastomer with tensile strength of 94.6 MPa and toughness of 310.4 MJ m-3, both of which far exceed that of any three-dimensional printed elastomer.